| 名稱 | 密度 | 成型收縮率 | UL94阻燃 | 產(chǎn)品描述及應(yīng)用 | 產(chǎn)品實例 |
| PEI 2212R | UL94V-0/0.4mm | 20％玻璃纖維增強，增強流動性，易脫模，阻燃 |
 |
|||
| PEI 2300 | 0.2-0.4/3.2mm(具體見物性大全) | UL94V-0/0.25mm UL94-5VA/1.21mm | 30％玻璃纖維增強，易流動，阻燃 |
 |
||
| PEI 2300R | 0.2-0.4/3.2mm | UL94V-0/0.25mm UL94-5VA/1.21mm | 30％玻璃纖維增強，易脫模，阻燃 |
 |
||
| PEI 2310 | 0.2-0.4/3.2mm(具體見物性大全) | UL94V-0/0.25mm UL94-5VA/1.21mm | 30％玻璃纖維增強，增強流動性，阻燃 |
 |
||
| PEI 2310EPR | 1.48 | 0.4-0.6/3.2mm(具體見物性大全) | UL94V-0/0.4mm | 30％玻璃纖維增強，高流動性，易脫模，阻燃。 |
 |
|
| PEI 2310R | UL94V-0/0.25mm UL94-5VA/1.21mm | 30％玻璃纖維增強，增強流動性，易脫模，阻燃 |
 |
|||
| PEI 2312 | 0.3-0.4/3.2mm(具體見物性大全) | UL94V-0/0.81mm | 30％玻璃纖維增強，增強流動性，阻燃 |
 |
||
| PEI 2312EPR | 1.48 | UL94HB/0.4mm | 30％玻璃纖維增強，高流動性，易脫模，阻燃 |
 |
||
| PEI 2313 | 0.3-0.4/3.2mm(具體見物性大全) | UL94V-0/0.35mm | 30％玻璃纖維增強，增強流動性，阻燃 |
 |
||
| PEI 2400 | 0.1-0.3/3.2mm | UL94V-0/0.25mm | 40％玻璃纖維增強，易流動，阻燃 |
 |
||
| PEI 2410 | 0.1-0.3/3.2mm | UL94V-0/0.25mm UL94-5VA/1.47mm | 40％玻璃纖維增強，增強流動性，阻燃 |
 |
||
| PEI 2410EPR | 1.56 | 0.2-0.4/3.2mm(具體見物性大全) | UL94 V-0 | 40％玻璃纖維增強，高流動性，易脫模，阻燃 |
 |
|
| PEI 2410R | 0.1-0.3/3.2mm | UL94V-0/0.25mm UL94-5VA/1.47mm | 40％玻璃纖維增強，增強流動性，易脫模，阻燃 |
 |
||
| PEI 2412EPR | 1.56 | 0.2-0.4/3.2mm(具體見物性大全) | UL94 HB | 40％玻璃纖維增強，高流動性，易脫模，阻燃 |
 |
|
| PEI 3451 | 0.15-0.25/3.2mm(具體見物性大全) | UL94 HB | 45％玻璃纖維和礦物增強，標準流動性，尺寸穩(wěn)定 |
 |
||
| PEI 3452 | 0.15-0.25/3.2mm(具體見物性大全) | UL94V-0/0.78mm UL94-5VA/2.99mm | 45％玻璃纖維和礦物增強，增強流動性，尺寸穩(wěn)定，阻燃 |
 |
||
| PEI 4000 | 0.2-0.3/3.2mm | UL94V-0/0.83mm | 玻璃纖維+石墨+PTFE，阻燃 |
 |
||
| PEI 4001 | 0.5-0.7/3.2mm | UL94V-0/0.38mm UL94-5VA/1.49mm | PTFE填充，標準流量聚醚酰亞胺 |
 |
||
| PEI 4211 | UL94 V-0 | 20％玻璃纖維增強 |
 |
|||
| PEI 8015 | 0.4-0.5/3.2mm(具體見物性大全) | UL94 HB | 高流動性 |
 |
||
| PEI 9011 | 1.27 | 0.5-0.7/3.2mm(具體見物性大全) | UL94 V-0 | 高流動性，改進加工光纖擠壓。 |
 |
|
| PEI 9075 | 0.5-0.7/3.2mm(具體見物性大全) | 高流動聚醚混合 |
 |
|||
| PEI 9076 | 0.5-0.7/3.2mm(具體見物性大全) | UL94 HB | 聚醚酰亞胺共混物，標準流量 |
 |
||
| PEI 9085 | 1.34 | 0.5-0.7/3.2mm | UL94 V-0 | 高流動聚醚混合 |
 |
|
| PEI AR9100 | 0.5-0.6/3.2mm | UL94 V-0 | 10％玻璃纖維增強，標準流量 |
 |
||